Product Description
We offer extruded PVDF (Polyvinylidene Fluoride) film with thickness from 10 um (0.4 mil) to 1,000 um (40 mil) in small rolls for R&D and product Development.
No minimal order quantity MOQ. Most thickness in stock.
Typical width: any width below 600 mm (wider film with 4-8 weeks lead time)
Typical thickness: better than +/-5%, 10 um, 15 um, 20 um, 30 um, 50 um, 75 um, 100 um, 125 um, 200 um, 300 um, 500 um, 1,000 um
Typical performance:
Surface Finish: gloss/gloss, gloss/Matte
Melting Temperature: 170-175 deg C
Density: 1.75~1.80 g/cc
Modulus: >1,800 MPa
Tensile Strength at yield: > 50 MPa
Tensile Strength at break: > 30 MPa
Elongation at Break: >300%
Dielectric Constant: ~12 at 1kHz and 25 C
Dielectric Loss: ~0.02 at 1 kHz and 25 C
Volume Resistivity: 10^13 ohm-cm
Thermal conductivity: 0.20 W/m/K
Vicat Softening Temperature: > 135 C