Product Description
Perfect ferroelectric relaxor composition, high dielectric constant, slim hysteresis, dielectric breakdown > 300 MV/m, used for high energy density capacitor, electrocaloric cooling ECE or actuator
CFE content is ~7mol%, optimized composition for K>50 at 25 C and 100 Hz
Melting Temperature: 125-135 C
Young's Modulus at 20 C: 150-250 MPa
Size 200 mm x 270 mm. Maybe on metallized PET film, the aluminum on PET is 1 ohm/sq, and the terpolymer coating is 3 um or 4.5 i,. Terpolymer can be removed with acetone or MEK to expose the bottom aluminum electrode.
Metallized PET is 50.8 um thick.
contact us for order > 3 pieces. Film is produced in 200 mm wide and in rolls with length >50 m. Let us know if you need >10 m long.
Special thickness/width production with lead time of 1 week.
Thickness ~3 um, ~4.5 um
Relaxor Ferroelectric Ferrorelaxor Terpolymer